PA12 + 15CF filament from ROSA3D is a combination of nylon and carbon fibers. The combination of the advantages of these two raw materials results in a product with extraordinary strength properties. PA12+15CF filament prints have the ability to work continuously at a temperature of over 160oC. PA+15CF prints can be successfully used as a replacement for steel elements to reduce the weight of the device, or construction. The PA+15CF filament is characterized by ease of printing and, thanks to the carbon fiber filling, low processing shrinkage. Recommended especially for semi-professionals and for advanced users. When printing PA12+15CF, hardened steel nozzles are recommended (brass and aluminum nozzles may be subject to abrasion), suggested nozzle size > 0.3 mm. Recommended printing temperature 250-290 oC. Recommended temperature table: 100-120oC
TECHNICAL PARAMETERS PA12 + 15CF
Diameter (mm): 1.75mm- Diameter tolerances (mm): +/- 0.05 mm
- Ovality tolerances (mm): +/- 0.02 mm
- Weight (g): 1000 g (vacuum packed with desiccant)
- Printing temperature (°C): 250-290°C
- Table temperature (°C): 100-120°C
PHYSICAL PARAMETERS PA + 15CF
- Density: 1.05g/cm3
- Smell: odorless
- Charpy impact strength:
- Unnotched - 55 kJ/m2 (ISO 179-1eU) Notched - 15 kJ/m2 (ISO 179-1eA)
- Tensile elongation (speed 5 mm/min, to break): 7% (ISO 527)
- Tensile strength (speed 5 mm/min, to break): 50 MPa (ISO 527)
- Tensile modulus (speed 1 mm/min): 3650 MPa (ISO 527)
- Vicat softening point: 168°C (ISO 306)